Snowflakes are white and sticky. Cause: the humidity of the stickers is too high. Solution: Because pasting paper is made of white latex, and the water content of white latex is high, so after the sticker, the resin coating can be carried out after a long time.

1, Snow White sticky hands

Formation reason: sticker humidity is too high.

Solution: Because pasting paper is made of white latex, and the water content of white latex is high, so after the sticker, the resin coating can be carried out after a long time.

Cause: The operating environment temperature is too low

Solution: Some heating measures can be used to raise the ambient temperature

Formation reason: the humidity of the air is too high.

Solution: The board should not be placed for too long after drying, easy to return to damp, should be used as soon as possible.

Formation reason: improper selection of accelerator, curing agent or its poor quality.

Solution: The general use of 5%, 6% concentration of cobalt water and high quality, small water content of curing agent. The gelling time is generally controlled in 4 ~ 6 minutes, and the amount of curing agent is generally 2.5 ~ 3 in the amount of cobalt water.

2. The resin layer is too brittle

Cause of formation: excessive dosage of accelerators and curing agents

Solution: reduce the amount of accelerator curing agent, the gelling time is generally controlled in 4 ~ 6 minutes, the curing agent amount is generally 2.5 ~ 3 in the amount of cobalt water

3. The resin layer is too soft

Formation reason: accelerant, curing agent dosage is too little

Solution: Increase the amount of accelerator curing agent, the gelling time is generally controlled in 4 ~ 6 minutes, the curing agent amount is generally 2.5 ~ 3 in the amount of cobalt water

4, the surface brightness is poor, fullness is poor

Formation reason: the effect of film type

Solution: There are many kinds of film, which must be selected according to their own requirements.

Formation reason: coating thickness influence

Solution: The fullness of general thick coating is better than thin coating.

Formation reason: the selection of resin viscosity influence.

Solution: The thickness of the film formed by the resin with high viscosity is better.

Related news

Unsaturated polyester resin classification and product introduction

Unsaturated polyester resin classification and product introduction

2023-10-27

Unsaturated polyester resin classification and product introduction

Unsaturated polyester resin classification and product introduction

2023-10-27

Share

Return list